Structure of polymerizable lipid bilayers. V. Synthesis, bilayer structure and properties of diacetylenic ether and...

Four diacetylenic phosphatidylcholines (PC's) have been synthesized and the structures of bilayers of these lipids have been determined at low resolution by low-angle X-ray diffraction. The PC's all have 18-carbon chains but differ with respect to the ether/ester linkage at the sn-1 and sn-2 positions and the relative position of the diacetylene moiety: diester-PC (1): 1,2-bis(octadeca-4',6'-diynoyl)-sn-glycero-3-phosphocholine diester-PC (2): 1-(octadeca-4',6'-diynoyl)-2-(octadeca-5',7'-diynoy l)-sn- glycero-3-phosphocholine diester-PC (3): 1,2-bis(octadeca-8',10'-diynoyl)-sn-glycerol-3-phosphocholin e diether-PC (4): 1-O-(octadeca-4',6'-diynyl)-2-O-(octadeca-5",7"-din yl)-sn- glycero-3-phosphocholine Only (1) exhibits the typical bilayer profile, whereas (2), (3) and (4) show evidence of interdigitation and/or significant disorder. Only (1) polymerized effectively upon illumination with 254 nm light, turning deep blue in seconds, indicating the formation of long, well-ordered polydiacetylenic structures. Liposomes of these derivatives were tested for permeability by osmotic swelling. Polymerized liposomes of (1) underwent osmotic swelling with urea, glycerol, and acetamide more rapidly than did liposomes of stearoyl-oleoyl-PC, but the initial rates of osmotic swelling of polymerized liposomes of (1) were 3-10-times lower than those of unpolymerized liposomes of (1). Blue polymerized multilayer samples of (1) exhibited an irreversible thermochromic transition to red at approx. 40 degrees C. Differential scanning calorimetry with liposome suspensions of (1) revealed an endotherm at 28.3 degrees C with a transition enthalpy of 40 J/g. PC (1) is a potentially useful diacetylenic lipid which exhibits facile, complete polymerization and a bilayer thickness comparable to that of biomembrane lipids.