Collagen ultrastructure in ruptured cruciate ligaments. An electron microscopic investigation

The ultrastructure of collagen fibrils was investigated in normal (n 39) and ruptured (n 23) human anterior cruciate ligaments. The normal ligament had a complex three-dimensional structure. Collagen fibrils predominantly had a undirectional course with parallel arrangement and a mean diameter of 75 (20-185) nm. Four days after anterior cruciate ligament rupture, the mean fibril diameter was increased; it later decreased, probably due to synthesis of young, thin 30-40 nm fibrils. Interfibrillar dysplastic collagen fibrils were detected in the extracellular matrix of ruptured ligaments. They were more frequently found later than 3 days after rupture and were seen also at a distance of 2-3 cm from the rupture zone. The presence of dysplastic fibrils may explain the functional insufficiency of the repair tissue in ruptured cruciate ligaments.