The nature of the structural gradient in epoxy curing at a glass fiber/epoxy matrix interface using FTIR imaging

The curing process of an epoxide system was studied at the interface formed between a silane-coated glass fiber and an epoxy matrix. The gradient in the structure of the epoxy resin as a result of the cure process at the fiber/matrix interfacial region was monitored by FTIR imaging. For comparison, the epoxy curing at the interface formed between the epoxy resin and (a) an uncoated glass fiber and (b) a polyorganosiloxane (obtained from the silane used for the glass-fiber coating) were also monitored. Chemically specific images of the OH and the H-N-H groups near the interface region were obtained. These images suggest that there is a chemical gradient in the structure of the matrix from the fiber surface to the polymer bulk due to different conversions. The basis of the different kinetics of the curing reactions is a result of amino group inactivation at the interface. This deactivation translates into an off-stoichiometry of the reaction mixture, which is a function of the distance from the surface of the glass fiber.