Assessing the performance of a methyl methacrylate-based resin cement with self-etching primer for bonding...

Questions over the usefulness of a self-etching primer with resin adhesive in the bonding of orthodontic brackets remain unsolved. The purpose of this study was to determine the effects of using Multibond, a new methyl methacrylate (MMA)-based resin cement with self-etching primer, on the shear bond strength of orthodontic brackets compared with Superbond C&B, which is a well-known MMA-based resin cement containing phosphoric acid etching. Metal or plastic brackets were bonded to etched or self-etching primed bovine teeth using Superbond C&B or Multibond. The shear bond strengths were measured after immersion in water at 37 degrees C for 24 hours. Data were analyzed by two-way analysis of variance and Scheffe's test. The surface appearances of the teeth after phosphoric acid etching or self-etching priming were observed by field-emission scanning electron microscopy (FE-SEM). Metal brackets bonded with Multibond had a significantly lower shear bond strength than metal brackets bonded with Superbond C&B. No significant differences in shear bond strength were observed between Multibond and Superbond C&B when plastic brackets were bonded to the enamel. The shear bond strength of metal brackets bonded with Multibond was comparable with that of plastic brackets bonded with Superbond C&B. Adhesive remnant index score showed a tendency of more residual resin cement remaining on the teeth when metal brackets were bonded with Multibond. FE-SEM observation revealed less dissolution of the enamel surface resulting from treatment with Multibond self-etching primer as compared with phosphoric acid. Thus, the Multibond system may be a candidate for bonding orthodontic brackets with the advantage of minimizing enamel loss.