Star-shaped azo-based dipolar chromophores: design, synthesis, matrix compatibility, and electro-optic activity

Three new azo-benzene-based push-pull chromophores with dendritic architecture were synthesized as active materials for electro-optic applications. These chromophores were synthesized in six or seven synthetic steps with an overall yield of around 80% per step and high purity. UV-vis spectroscopy showed significant influence of the transient dipole moment on the observed r(33) values. The chromophores were stable to photochemical oxidation in ambient light and air. The electrical poling conditions were optimized for each chromophore as the T(g) of the composite material varied significantly. The highest EO coefficient achieved was 22-25 pm/V at 1550 nm wavelength. STEM analysis of the blends enabled the correlation of the activity of these large chromophores with the blend morphology. An amorphous polycarbonate host effectively disperses the chromophores in 2-20 nm aggregates in the active materials. However, macrophase separation into 200-500 nm aggregates was observed in a methacrylate host matrix.