Citrate increases glass transition temperature of vitrified sucrose preparations

The aim of this study was to investigate the effect of sodium citrate on the properties of dried amorphous sucrose glasses. Addition of sodium citrate to a sucrose solution followed by freeze-drying or convective drying resulted in a glass transition temperature (Tg) that was higher than the well-studied sucrose Tg. This result was obtained either at reduced water content of the analysed sample or by removal of water during Modulated DSC analysis. After removal of the remaining water ( < 3.5% w/w), a Tg of approximately 105 degrees C was obtained at a mass ratio of sodium citrate to sucrose of 0.3. FTIR analysis showed a similar increase in Tg as was found with Modulated DSC analysis. The Tg values were derived from breaks in the vibrational frequency vs. temperature plots in the OH stretching and bending regions. Elevated average strength of hydrogen bonding in the sucrose/citrate glass was concluded from the downshift of the OH stretching band of 25 cm(-1) and from the reduced wavenumber temperature coefficient (WTC). The antisymmetric carboxylate stretch of citrate sensed the glass transition of the mixture, from which we conclude that citrate interacts with the sucrose OH via its carboxylate groups.