Optical properties of structurally modified glasses doped with gold ions

We report on the optical properties of a structurally modified silicate glass doped with Au ions. The area in the vicinity of the focal point of an 800-nm femtosecond laser in a glass sample became gray as a result of the formation of color centers after laser irradiation and turned red because of precipitation of Au nanoparticles after further annealing at 550 degrees C for 30 min. When the glass was excited by UV light at 365 nm, yellowish-white and orange-yellow emissions were observed in the laser-irradiated and the Au-nanoparticle-precipitated area, respectively. An optical Kerr shutter experiment showed that the Au nanoparticle-precipitated glass had an ultrafast nonlinear optical response, and the third-order nonlinear susceptibility was estimated to be approximately 10(-11) esu.