Synthesis of atomically ordered AuCu and AuCu(3) nanocrystals from bimetallic nanoparticle precursors

A new multistep approach was developed to synthesize atomically ordered intermetallic nanocrystals, using AuCu and AuCu(3) as model systems. Bimetallic nanoparticle aggregates are used as precursors to atomically ordered nanocrystals, both to precisely define the stoichiometry of the final product and to ensure that atomic-scale diffusion distances lower the reaction temperatures to prevent sintering. In a typical synthesis, PVP-stabilized Au-Cu nanoparticle aggregates synthesized by borohydride reduction are collected by centrifugation and annealed in powder form. At temperatures below 175 degrees C, diffusion of Cu into Au occurs, and the atomically disordered solid solution Cu(x)Au(1)(-)(x) exists. For AuCu, nucleation occurs by 200 degrees C, and atomically ordered AuCu exists between 200 and 400 degrees C. For AuCu(3), an AuCu intermediate nucleates at 200 degrees C, and further diffusion of Cu into the AuCu intermediate at 300 degrees C nucleates AuCu(3). Atomically ordered AuCu and AuCu(3) nanocrystals can be redispersed as discrete colloids in solution after annealing between 200 and 300 degrees C.