Bulk interfaces in a Ni-rich Ni-Au alloy investigated by high-resolution Z-contrast imaging

Interfaces between Au-rich precipitates and the Ni-rich matrix in a decomposed Ni-10 at.% Au alloy were investigated by low-magnification and high-resolution Z-contrast imaging. During aging at 923 K, the originally single crystalline sample decomposed and recrystallized resulting in a microstructure consisting of subgrains separated by small-angle grain boundaries. These small-angle grain boundaries are decorated by Au-rich precipitates. The interfaces between the Au-rich precipitates and the Ni-rich matrix were characterized with respect to the orientation relationship between precipitates and matrix, misfit dislocations and concentration gradients. Two transformation modes were identified that are involved in the decomposition of bulk Ni-rich Ni-Au alloys. While in the first mode the interface is semi-coherent, in the second mode the interface corresponds to an incoherent twin boundary. It is further shown that strain fields around misfit dislocations can result in systematic errors in the determination of the concentration gradients across interfaces between precipitates and matrix.