Enhanced wear performance of ultra high molecular weight polyethylene crosslinked by organosilane

C Y Tang1, X L Xie, X C Wu

  • 1Department of Industrial and Systems Engineering, The Hong Kong Polytechnic University, Kowloon, Hong Kong, PR China mfcytang@polyu.edu.hk

Journal of Materials Science. Materials in Medicine
|September 7, 2004
PubMed

More Related Videos

Improved Polydimethylsiloxane (PDMS) Double Casting via Silicone Oil Treatment for Densely Packed Microstructure Replication07:01

Improved Polydimethylsiloxane (PDMS) Double Casting via Silicone Oil Treatment for Densely Packed Microstructure Replication

Published on: July 18, 2025

Light-induced Patterning and Grafting for Slippery Surfaces based on Silane-coated Nanoporous Structures07:23

Light-induced Patterning and Grafting for Slippery Surfaces based on Silane-coated Nanoporous Structures

Published on: November 14, 2025

Related Concept Videos

Olefin Metathesis Polymerization: Overview01:13

Olefin Metathesis Polymerization: Overview

Recently, the development of olefin metathesis polymerization advanced the field of polymer synthesis. Simply put, the reorganization of substituents on their double bonds between two olefins in the presence of a catalyst is known as the olefin metathesis reaction. The use of metathesis reaction for polymer synthesis is called olefin metathesis polymerization.
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists of a...
Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)00:53

Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)

Acyclic diene metathesis polymerization or ADMET polymerization involves cross-metathesis of terminal dienes, such as 1,8-nonadiene, to give linear unsaturated polymer and ethylene. As ADMET is a reversible process, the formed ethylene gas must be removed from the reaction mixture to complete the polymerization process.
Similar to cross-metathesis, ADMET also involves the formation of metallacyclobutane intermediate by [2+2] cycloaddition of one of the double bonds of a terminal diene with...
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta catalyst, high molecular...
Classification and Mechanical Properties of Synthetic Polymers01:28

Classification and Mechanical Properties of Synthetic Polymers

Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...