Degradation behavior of poly(epsilon-caprolactone)-b-poly(ethylene glycol)-b-poly(epsilon-caprolactone) micelles in...

Poly(epsilon-caprolactone)-b-poly(ethylene glycol)-b-poly(epsilon-caprolactone) triblock copolymers were synthesized by the ring-opening polymerization of epsilon-caprolactone in the presence of hydroxyl-terminated poly(ethylene glycol) with different molecular weights, using stannous octoate catalyst. Micelles prepared by the precipitation method with these triblock copolymers exhibit a core-shell structure. The degradation behaviors of these core-shell micelles in aqueous solution were investigated by FT-IR, 1H NMR, GPC, DLS, TEM, and AFM. It was found that the degradation behavior of micelles in aqueous solution was quite different from that of bulk materials. The size of the micelles increased in the initial degradation stages and decreased gradually when the degradation period was extended. The caprolactone/ethylene oxide (CL/EO) ratio in micelles measured by NMR also shows an increase at the initial degradation stage and a decrease at later stages. The morphology of these micelles became more and more irregular during the degradation period. We explain the observed behavior by a two-stage degradation mechanism with interfacial erosion between the cores and the shells followed by core erosion.