In vitro and in vivo hemocompatibility evaluation of graphite coated polyester vascular grafts

Attempts have been made in this study to prepare a homogeneous and stable coating of graphite on polyester vascular grafts (GPVG) using an electrophoresis method to evaluate thromboresistant and blood compatibility of GPVG in comparison to non-coated PVG and InterGard (collagen sealed PVG) as control. Lactate dehydrogenase (LDH) activity measurement was carried out on all PVG types to evaluate platelet adhesion. To examine tissue reaction GPVG and non-coated sheets of knitted polyester fabric were implanted simultaneously in the dorsal flank of rats subcutaneously. The GPVG, non-coated and control were implanted in descending aorta as end-to-end or end-to-side implantation substitution in 25 sheep for 4-60 weeks. Results showed that the graphite coating on polyester vascular grafts reduced the number of adherent platelets and prevent platelet activation and spreading on the surface in comparison with non-coated and control. Pathological investigation showed inflammatory reactions were totally resolved after 12 weeks and there was no difference in the tissue reaction between graphite coated, non-coated and control patches. All grafts remained patent and there was no significant difference in patency rate between these three types of PVG. We found that GPVG has no need for pre-clotting and it showed lower platelet aggregation, thinner capsule formation and lower calcification after 15 months. However, suturing of GPVG was more difficult in comparison with the other types.