Hardness and compressive strength of indirect composite resins: effects of immersion in distilled water

A Da Fonte Porto Carreiro1, C A Dos Santos Cruz, C E Vergani

  • 1Department of Dental Materials and Prosthodontics, São Paulo State University, Araraquara Dental School, Araraquara, S.P., Brazil. adrianadafonte@hotmail.com

Journal of Oral Rehabilitation
|November 5, 2004
PubMed

Keywords:
dental composite materialswater aging effectsmechanical properties of dentistryrestorative material testing

More Related Videos

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials05:30

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials

Published on: January 10, 2025

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Related Concept Videos

Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to the...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in the...
Testing Water Quality01:14

Testing Water Quality

When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
Drying Shrinkage01:21

Drying Shrinkage

When hardened concrete is exposed to air with a relative humidity of less than 100 percent, it begins to lose the free water within its capillaries. As this water evaporates, the water initially adsorbed onto the calcium silicate hydrates migrates towards these now empty spaces and eventually evaporates as well. Over time, as more water leaves, the volume of the concrete decreases, a phenomenon known as drying shrinkage.
A portion of this drying shrinkage can be reversed; if the concrete is...
Effect of Sea Water on Concrete01:22

Effect of Sea Water on Concrete

Concrete exposed to seawater can undergo degradation like the dissolution of ettringite and gypsum, increasing the material's porosity and decreasing its strength. In contrast, the crystallization of salts within the concrete's pores can cause expansion, particularly above the waterline where evaporation occurs. Nonetheless, this expansion only happens when seawater, enabled by the concrete's permeability, manages to infiltrate the structure.
Concrete in areas between tide marks, which undergo...