The first metal (Nd3+, Mn2+, and Pb2+) coordination compounds of 3,5-dinitrotyrosine and their nonlinear optical properties

The reactions of 3,5-dinitrotyrosine (H2DNTY) with Nd(NO3)3.6H2O, Mn(ClO4)2.6H2O, and Pb(OAc)2 afforded three homochiral compounds: discrete [Nd(Hdnty)2(NO3)(H2O)5].3H2O (1) and two- and three-dimensional coordination polymers, [Mn(Hdnty)2] (2) and [Pb(dnty)(0.5 H2O)] (3), respectively. The Nd atom in 1 displays a tricapped trigonal prism and supramolecular weak interactions, such as pi-pi stacking and H-bonds, between amino and nitro groups result in the formation of a three-dimensional network through these interactions. 2 has a two-dimensional square-grid topological net while 3 has the first three-dimensional homochiral ThSi2 net. To the best of our knowledge, these are the first metal coordination compounds with 3,5-dinitrotyrosine. Preliminary second harmonic generation (SHG) investigations indicated that 1 and 2 are SHG active with estimated responses 5 and 6 times larger than that of urea, respectively, while 3 is SHG non-active (obeying the Klainman symmetry requirement). Strong enhancement of their SHG efficiency, compared with H2DNTY, may be due to 1) the addition of a good donor-pi-acceptor organic chromophore into the compound resulting in superior qualities of both inorganic and organic materials and 2) the H-bonds that persist in them. Crystal data: 1: C18H32N7O25Nd, Mr = 890.75 g mol(-1), monoclinic, P2(1), a=7.0179(7), b=27.060(3), c=8.3097(8) A, alpha=gamma=90.00, beta=95.646(2) degrees , V=1570.4(3) A(3), Z=2, rho(calcd)=1.884 Mg m(-3), R(1)=0.0489, wR(2)=0.1223, mu=17.67 mm(-1), S=0.811, Flack value=0.003(13); 2: C(18)H(16)N(6)O(14)Mn, M(r)=595.31 g mol(-1), orthorhombic, P2(1)2(1)2, a=8.4381(14), b=13.639(2), c=19.697(3) A, alpha=beta=gamma=90.00 degrees , V=2266.9(6) A(3), Z=4, rho(calcd)=1.744 Mg m(-3), R(1)=0.0866, wR(2)=0.2030, mu=6.72 mm(-1), S=1.095, Flack value=0.02(6); 3: C(9)H(8)N(3)O(7.5)Pb, M(r)=485.37 g mol(-1), tetragonal, P4(1)2(1)2, a=12.8136(12), b=12.8136(12), c=14.931(2), alpha=beta=gamma=90.00 degrees , V=2451.5(5) A(3), Z=8, rho(calcd)=1.885 Mg m(-3), R(1)=0.0564, wR(2)=0.1323, mu=6.942 mm(-1), S=0.878, Flack value=0.03(2). For space group P4(3)2(1)2: R(1)=0.0672, wR(2)=0.1656, S=1.034, Flack value=1.02(3); this suggests the chosen space group P4(1)2(1)2 is correct.