Aggregated structure analysis of polymer-protected platinum/ruthenium colloidal dispersions using EXAFS, HRTEM, and
Masafumi Harada1, Naoki Toshima, Kaname Yoshida
1Department of Textile and Apparel Science, Faculty of Human Life and Environment, Nara Women's University, Nara 630-8506, Japan. harada@cc.nara-wu.ac.jp
Abstract:
Polymer-protected platinum/ruthenium colloidal dispersions were prepared by refluxing mixed solutions of hexachloroplatinic(IV) acid and ruthenium(III) chloride in a mixture of ethanol/water (1/1 v/v) in the presence of poly(N-vinyl-2-pyrrolidone). The electronic spectra and transmission electron micrographs suggested that the colloidal dispersions are almost composed of the mixture of the small monometallic Pt and Ru clusters over all the ratio of Pt/Ru compositions. Extended X-ray absorption fine structure analyses and high resolution electron microprobe analyses indicated that no Pt/Ru alloy clusters exist in the dispersions, and the aggregation occurs between small monometallic Pt clusters (diameter ca. 15 A) and partially oxidized Ru microclusters (diameter less than 10 A). Electron diffraction measurements also suggested that the diffraction pattern of aggregated Pt/Ru cluster particles prepared by the simultaneous reduction of Pt and Ru ions is the same as that of the physical mixture of the small monometallic Pt and Ru clusters separately prepared. Therefore, it can be concluded that the aggregated Pt/Ru cluster particles, with 10 to 60 A in diameter, are built up by small monometallic Pt clusters and partially oxidized Ru microclusters, and that Pt/Ru alloy clusters are not formed.