Influence of polymer matrix and adsorption onto silica materials on the migration of alpha-tocopherol into 95%...

In this study, the effect of polymer materials with different polarity, namely low density polyethylene (LDPE) and ethylene vinyl acetate (EVA), on the migration behaviour of alpha-tocopherol from active packaging was investigated. The antioxidant was also adsorbed onto silica materials, namely SBA-15 (Santa Barbara-15) and Syloblock, in order to protect the antioxidant during extrusion and to ensure a controlled and sufficient release during the shelf-life of the food product. Migration experiments were performed at 7.0 +/- 0.5 degrees C and 95% ethanol was used as fatty food simulant. All films contained a high concentration of alpha-tocopherol, approximately 2000 mg kg(-1), to obtain an active packaging. Polymer matrix had a small influence on the migration profile. The migration of 80% of total migrated amount of antioxidant was retarded for 2.4 days by using LDPE instead of EVA. When alpha-tocopherol was adsorbed onto both silica materials, the migration of 80% of total migrated amount of antioxidant was retarded for 3.4 days in comparison to pure alpha-tocopherol. No difference was seen between the migration profiles of alpha-tocopherol adsorbed onto both silica materials. In the case of pure alpha-tocopherol, 82% of the initial amount of alpha-tocopherol in the film migrated into the food simulant at a rather fast migration rate. In the case of adsorption on silica materials, a total migration was observed. These antioxidative films can have positive food applications.