Glazed tiles manufactured from incinerated sewage sludge ash and clay

Deng-Fong Lin1, Huan-Lin Luo, Yeong-Nain Sheen

  • 1Department of Civil and Ecological Engineering, I-Shou University, Ta-Hsu Hsiang, Kaohsiung, Taiwan, Republic of China. dflin@isu.edu.tw

Journal of the Air & Waste Management Association (1995)
|March 31, 2005
PubMed

Keywords:
ceramic tile manufacturingwaste material utilizationincinerated sludge ashglaze concentration effects

More Related Videos

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography06:53

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography

Published on: January 25, 2019

Aesthetically Enhanced Silica Aerogel Via Incorporation of Laser Etching and Dyes08:21

Aesthetically Enhanced Silica Aerogel Via Incorporation of Laser Etching and Dyes

Published on: March 12, 2021

Related Concept Videos

Bricks01:14

Bricks

Bricks, a fundamental building material, are crafted from fired clay and exhibit a range of shapes, sizes, and colors. The production process starts with extracting local clay or shale, which is then crushed, ground, and screened for a fine texture. The refined material is blended with water, creating a pliable mixture that can be formed into bricks using one of three processes: soft mud, dry press, or stiff mud methods.
Soft mud bricks are shaped in molds with high moisture content and can be...
Manufacture of Concrete Masonry Units01:27

Manufacture of Concrete Masonry Units

The process of manufacturing concrete masonry units begins by mixing stiff concrete composed of Portland cement, aggregates, and water. This mixture is then poured into metal molds. To ensure the concrete settles uniformly and to avoid separation of its components, the mixture in the molds is subjected to vibration. Shortly after, the still-wet blocks are removed from the molds and placed on racks.
These wet blocks are then transported for curing, which can occur in one of two environments: a...
Cavity Drainage and Flashings in Masonry walls01:20

Cavity Drainage and Flashings in Masonry walls

Typically, a cavity wall consists of two wythes separated by a gap of at least 2 inches, which may contain insulation while still maintaining a minimum clear space of 1 inch to facilitate adequate drainage. Advanced methods like the insertion of a continuous drainage mat can further reduce this space while ensuring effective moisture expulsion.
Weep holes, strategically placed at the base of the cavity, are critical for draining accumulated water. These openings are created by leaving head...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is a...
Waterproofing and Anti-Bacterial Admixtures in Concrete01:22

Waterproofing and Anti-Bacterial Admixtures in Concrete

Concrete's susceptibility to water absorption is due to the capillary action within the pores of its hydrated cement paste. This action draws water in, creating the need for waterproofing admixtures to prevent such penetration. The efficacy of these admixtures is contingent upon the water pressure, with variations arising from different conditions such as rain, capillary rise, or hydrostatic pressure in structures intended to hold water.
Waterproofing admixtures render concrete hydrophobic,...