Azorhodanine derivatives as inhibitors for acidic corrosion of nickel

Abd El-Aziz S Fouda1, Ahmed A Al-Sarawy, Tark M Omar

  • 1Department of Chemistry, Faculty of Science, El-Mansoura University, El-Mansoura 35516, Egypt. asfouda@yahoo.com

Annali Di Chimica
|April 2, 2005
PubMed

More Related Videos

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area08:13

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

Published on: February 19, 2018

Effect of Microwave Synthesis Conditions on the Structure of Nickel Hydroxide Nanosheets07:57

Effect of Microwave Synthesis Conditions on the Structure of Nickel Hydroxide Nanosheets

Published on: August 18, 2023

Related Concept Videos

Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
Preparation of Amines: Reduction of Oximes and Nitro Compounds01:29

Preparation of Amines: Reduction of Oximes and Nitro Compounds

Oximes can be reduced to primary amines using catalytic hydrogenation, hydride reduction, or sodium metal reduction. The reduction of aliphatic and aromatic nitro compounds to primary amines takes place by either catalytic hydrogenation or by using active metals like Fe, Zn, and Sn in the presence of an acid.
Though catalytic hydrogenation can reduce nitrobenzenes, the reduction is nonselective in the presence of other functional groups. For instance, if nitrobenzene contains an aldehyde group,...
1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Overview01:26

1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Overview

Nitrous acid and nitric acids are two types of acids containing nitrogen, among which nitrous acid is weaker than nitric acid. Nitrous acid with a pKa value of 3.37 ionizes in water to give a nitrite ion and the hydronium ion.
The nitrous acid is unstable. Hence, it is formed in situ from a solution of sodium nitrite and cold aqueous acids such as hydrochloric or sulfuric acid. In an acidic solution, the –OH group of nitrous acid undergoes protonation to give oxonium ion, followed by water loss...
Diazonium Group Substitution: –OH and –H01:19

Diazonium Group Substitution: –OH and –H

Nitrous acid, a weak acid, is prepared in situ via the reaction of sodium nitrite with a strong acid under cold conditions. This nitrous acid prepared in situ reacts with primary arylamines to form arenediazonium salts. Such reactions are known as diazotization reactions. As shown in Figure 1, the formation of arenediazonium salts begins with the decomposition of nitrous acid in an acidic solution to give nitrosonium ions.
1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Mechanism01:37

1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Mechanism

Nitrous acid is a relatively weak and unstable acid prepared in situ by the reaction of sodium nitrite and cold, dilute hydrochloric acid. In an acidic solution, the nitrous acid undergoes protonation when it loses water to form a nitrosonium ion—an electrophile. Nitrous acid reacts with primary amines to give diazonium salts. The reaction is called diazotization of primary amines.
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...