Large area UV casting using diverse polyacrylates of microchannels separated by high aspect ratio microwalls

Large area molding of long and deep microchannels separated by high aspect ratio microwalls is important for high sensitivity and high throughput microfluidic devices. Ultraviolet (UV) casting is a feasible, economical and convenient method of replication of such microstructures in plastics. It is shown that a wide variety of polyacrylates with diverse properties such as those made from epoxy (EP), polyurethane (UR), polyester (ES), poly (ethylene glycol) (EG) and poly(propylene glycol) (PG) can be used for the high aspect ratio (7-9) UV casting of such linear microstructures over a 100 mm diameter, enlarging the range of applications of the replicated microstructures. Some challenges arise. With the EG formulation, wavy microstructures were observed; this can be overcome by stress relaxation. With non-polar PG formulation, poor adhesion between the polyester substrate and resin can lead to delamination of the casting from the substrate during demolding; this can be overcome by pre-coating a partially cured same resin on the polyester substrate. An optimum UV irradiation time was important for cure at the deepest end of the microstructure without excessive crosslinking leading to much increased demolding forces. The viscosity and wetting capability of the formulations were found to affect replication fidelity.