Long-range ordered thin films of block copolymers prepared by zone-casting and their thermal conversion into ordered...

Large-scale alignment of lamellae in thin films of diblock copolymers containing polyacrylonitrile and poly(n-butyl acrylate) was achieved by casting copolymer solution on a silicon substrate moved away at a constant speed from the casting nozzle (zone-casting). Grazing incidence small-angle X-ray scattering revealed that the lamellae, which were perpendicular to the substrate, were also aligned over macroscopic scale in the direction perpendicular to the casting direction. Such long-range ordered block copolymer films were then converted by pyrolysis into nanostructured carbons, with excellent preservation of lamellar morphology and orientation.