Selective functionalization of In2O3 nanowire mat devices for biosensing applications

A strategy to covalently attach biological molecules to the electrochemically active surface of indium oxide nanowire (In2O3 NW) mat devices is presented. A self-assembled monolayer (SAM) of 4-(1,4-dihydroxybenzene)butyl phosphonic acid (HQ-PA) was generated on an indium tin oxide (ITO)-coated glass and In2O3 NWs surface. The chemical steps required for surface derivatization were optimized on an ITO surface prior to modifying the In2O3 NWs. The hydroquinone group contained in the HQ-PA SAM was electrochemically oxidized to quinone (Q-PA) at +330 mV. The monolayer of Q-PA was allowed to react with a thiol-terminated DNA. The DNA was paired to its complementary strand tagged with a fluorescence dye. Attachment of DNA was verified using fluorescence microscopy. A device was subsequently prepared on a SiO2-supported mat of In2O3 NWs by depositing gold electrodes on the mat surface. The reaction strategy optimized on ITO was applied to this In2O3 NW-based device. Arrays of In2O3 NWs on a single substrate were electrochemically activated in a selective manner to Q-PA. Activated In2O3 NWs underwent reaction with HS-DNA and gave a positive fluorescence response after pairing with the dye-DNA. The unactivated In2O3 NWs gave no response, thus demonstrating selective functionalization of an In2O3 NW array. This can be considered a key step for the future fabrication of large-scale, inexpensive, nanoscale biosensors.