Effect of dynamic loading on the frictional response of bovine articular cartilage

The objective of this study was to test the hypotheses that (1) the steady-state friction coefficient of articular cartilage is significantly smaller under cyclical compressive loading than the equilibrium friction coefficient under static loading, and decreases as a function of loading frequency; (2) the steady-state cartilage interstitial fluid load support remains significantly greater than zero under cyclical compressive loading and increases as a function of loading frequency. Unconfined compression tests with sliding of bovine shoulder cartilage against glass in saline were carried out on fresh cylindrical plugs (n=12), under three sinusoidal loading frequencies (0.05, 0.5 and 1 Hz) and under static loading; the time-dependent friction coefficient mu(eff) was measured. The interstitial fluid load support was also predicted theoretically. Under static loading mu(eff) increased from a minimum value (mu(min)=0.005+/-0.003) to an equilibrium value (mu(eq)=0.153+/-0.032). In cyclical compressive loading tests mu(eff) similarly rose from a minimum value (mu(min)=0.004+/-0.002, 0.003+/-0.001 and 0.003+/-0.001 at 0.05, 0.5 and 1 Hz) and reached a steady-state response oscillating between a lower-bound (mu(lb)=0.092+/-0.016, 0.083+/-0.019 and 0.084+/-0.020) and upper bound (mu(ub)=0.382+/-0.057, 0.358+/-0.059, and 0.298+/-0.061). For all frequencies it was found that mu(ub)>mu(eq) and mu(lb)