Pyrogenic iron(III)-doped TiO2 nanopowders synthesized in RF thermal plasma: phase formation, defect structure, band...

Iron(III)-doped TiO(2) nanopowders, with controlled iron to titanium atomic ratios (R(Fe/Ti)) ranging from nominal 0 to 20%, were synthesized using oxidative pyrolysis of liquid-feed metallorganic precursors in a radiation-frequency (RF) thermal plasma. The valence of iron doped in the TiO(2), phase formation, defect structures, band gaps, and magnetic properties of the resultant nanopowders were systematically investigated using Mössbauer spectroscopy, XRD, Raman spectroscopy, TEM/HRTEM, UV-vis spectroscopy, and measurements of magnetic properties. The iron doped in TiO(2) was trivalent (3+) in a high-spin state as determined by the isomer shift and quadrupole splitting from the Mössbauer spectra. No other phases except anatase and rutile TiO(2) were identified in the resultant nanopowders. Interestingly, thermodynamically metastable anatase predominated in the undoped TiO(2) nanopowders, which can be explained from a kinetic point of view based on classical homogeneous nucleation theory. With iron doping, the formation of rutile was strongly promoted because rutile is more tolerant than anatase to the defects such as oxygen vacancies resulting from the substitution of Fe(3+) for Ti(4+) in TiO(2). The concentration of oxygen vacancies reached a maximum at R(Fe/Ti) = 2% above which excessive oxygen vacancies tended to concentrate. As a result of this concentration, an extended defect like crystallographic shear (CS) structure was established. With iron doping, red shift of the absorption edges occurred in addition to the d-d electron transition of iron in the visible light region. The as-prepared iron-doped TiO(2) nanopowders were paramagnetic in nature at room temperature.