Noncontact atomic force microscopy studies of ultrathin films of amorphous solid water deposited on Au(111)

Noncontact atomic force microscopy was used to study the morphological changes of an ultrathin amorphous solid water (ASW) film as a function of deposition temperature, annealing temperature, and annealing time. ASW deposited at 80 or 108 K on Au(111) formed truncated hemispherical clusters of increasing size during annealing at 134 K; these clusters were inferred to be crystalline. The number of nuclei present at the outer surface of the film after deposition was greater for higher deposition temperature. For lower cluster densities, depletion of the ASW film around the clusters was observed when the clusters became larger and dendritic growth was observed when the apparent cluster footprint radius exceeded 100 nm.