ATR-FTIR investigation on the complexation of myo-inositol hexaphosphate with aluminum hydroxide

The adsorption isotherm of and the pH effect on the adsorption of myo-inositol hexaphosphate (myo-IP6) on amorphous aluminum hydroxide was investigated. It was found that the adsorption isotherm of myo-IP6 on aluminum hydroxide could be well fitted with the Freundlich isotherm. The amount of myo-IP6 adsorbed remained almost constant in the range of pH 4.0 to 7.0, but it decreased considerably as the initial pH was over 7. The adsorption of myo-IP6 resulted in an increase in the pH level due to the release of OH(-) ions, which suggested that the adsorption of myo-IP6 on aluminum hydroxide was caused by a ligand exchange reaction. ATR-FTIR analysis of myo-IP6 in solution and adsorbed on aluminum hydroxide at different pH were performed. The ATR-FTIR investigation indicated that myo-IP6 was adsorbed onto aluminum hydroxide by forming inner-sphere complexes and adsorption facilitated the deprotonation of phosphate groups. The asymmetric vibration of the PO bond in AlPO(-)(3) appearing at a lower frequency than that in the terminal HPO(-)(3) indicated that Al bound to the O atom not as strongly as the H atom did. The ATR-FTIR investigation and theoretical calculation (with the Gaussian 03 program) revealed that three of the six phosphate groups in myo-IP6 molecules were bound to aluminum hydroxide while the other three remained free when myo-IP6 was adsorbed on aluminum hydroxide.