An evaluation of the performance of porous polymer monolith assisted electrospray

A novel electrospray interface, which has distinct advantages over conventional pulled silica emitters, has been developed. This novel interface can be easily fabricated by forming a porous polymer monolith (PPM) at the end of a fused-silica capillary that facilitates a stable electrospray over a wide range of flow rates with only a modest increase in back-pressure. A comparison was made between the PPM-assisted electrospray and a commercial nanosprayer in terms of sensitivity, stability and robustness. A PPM-filled electrospray tip produced a day-to-day signal variation of 23% relative standard deviation (RSD) over a 3-day period when spraying a 1.0 microM test peptide solution. Furthermore, three different capillaries fabricated by the same process produced a signal variation of 17% RSD, indicating that the fabrication process shows good reproducibility. The multiple flow paths of the PPM function to split the flow and reduce clogging. Even following the accumulation of debris after prolonged use, a stable spray could still be generated with the PPM-filled capillary while the commercial nanosprayer ceased to function properly. In terms of sensitivity, PPM-assisted electrospray showed an enhancement in sensitivity at infusion flow rates between 100 to 1000 nL/min while commercial nanosprayers performed slightly better at flow rates below 100 nL/min. A sample purification step can be combined with the PPM-assisted sprayer, using the PPM as a stationary phase to desalt and preconcentrate samples prior to mass spectrometric detection.