Atomic force microscopy of collagen structure in bone and dentine revealed by osteoclastic resorption

Mineralised tissues such as bone consist of two material phases: collagen protein fibrils, secreted by osteoblasts, form model structures for subsequent deposition of mineral, calcium hydroxyapatite. Collagen and mineral are removed in a three-dimensional manner by osteoclasts during bone turnover in skeletal growth or repair. Bone active drugs have recently been developed for skeletal diseases, and there is revived interest in changes in the structure of mineralised tissues seen in disease and upon treatment. The resolution of atomic force microscopy and use of unmodified samples has enabled us to image bone and dentine collagen exposed by the natural process of cellular dissolution of mineralised matrix. The morphology of bone and dentine has been analysed when fully mineralised and after osteoclast-mediated bone resorption, and compared with results from other microscopy techniques. Banded type I collagen, with 66.5+/-1.4 nm axial D-periodicity and 62.2+/-7.0 nm diameter, has been identified within resorption lacunae in bone and 69.4+/-4.3 nm axial D-periodicity and 140.6+/-12.4 nm diameter in dentine substrates formed by human and rabbit osteoclasts, respectively. This observation suggests a route by which the material and morphological properties of bone collagen can be analysed in situ, compared with collagen from non-skeletal sites, and contrasted in diseases of medical importance, such as osteoporosis, where skeletal tissue is mechanically weakened.