Raman spectroscopic study of a post-medieval wall painting in need of conservation

Raman spectroscopic studies of four specimens from an important angel wall painting in need of conservation work in a medieval church have provided some information about the pigments and pigment compositions which will influence possible future preservation and restoration strategies. Excitation of the Raman spectra at 1,064 nm in macroscopic mode and at 785 nm in microscopic mode revealed that the white pigment on the angel's wings was a mixture of barytes with calcite and lead white in minor composition. Although the specimens provided were not directly associated with coloured regions of the painting, yellow and blue microcrystals were found and they were identified as chrome yellow and lazurite, respectively. Red and brown particles were identified as cinnabar/vermilion and haematite. Several green particles were also found but could not be identified. The green and blue crystals could be related to neighbouring coloured regions of the artwork and the yellow colour could be identified as a background to the angel figure. Particles of carbon were found to be dispersed throughout the specimens and can be ascribed to soot from candles, heating stoves or oil lamps providing lighting in the church. No evidence for biological deterioration was found from the spectra. The unusual pigment palette is strongly suggestive of a later date of painting than was originally believed but there is a possibility that an earlier rendition exists underneath. Following a review of the spectroscopic data, a more extensive sampling protocol is recommended, from which some stratigraphic evidence could identify the underlying plaster and possible artwork.