Evaluation of a new fiber-reinforced resin composite

Efficacy of the usage of an experimental fiber-reinforced composite (FRC) on mechanical properties of an indirect composite was investigated by means of three-point bending and Charpy impact tests. Bond strength between the FRC and the indirect composite was also evaluated by tensile testing. The FRC consisted of a matrix resin with 25% silanized milled glass fiber (11-microm diameter, 150-microm length) and 5% colloidal silica. The values of strain of proportional limit, total strain, and fracture energy of the FRC during the bending test (1.2%, 10.4%, and 41.6 x 10(-3) J) were significantly higher than those of the indirect composite (0.1%, 2.5%, and 11.9 x 10(-3) J). The impact strengths of the 1-mm specimens with FRC ranged from 15.2 to 15.9 kJ/m(2), and were significantly higher than that of the control (3.1 kJ/m(2)). The 2-mm specimens showed significant difference from the control when the FRC thickness was equal or greater than 0.5 mm. The bond strength after the thermocycling was 15.2 MPa, and all of the specimens exhibited cohesive fracture inside the indirect composite. Based upon the results, it was concluded that the FRC tested in this study improved toughness and impact resistance of the indirect composite. The interfacial bonding between the FRC and the indirect composite was strong enough to prevent delamination.