Sorption and solubility testing of orthodontic bonding cements in different solutions

Manuel Toledano1, Raquel Osorio, Estrella Osorio

  • 1Department of Dental Materials, University of Granada, Avda Fuerzas Armadas, Granada, Spain. toledano@ugr.es

Journal of Biomedical Materials Research. Part B, Applied Biomaterials
|September 30, 2005
PubMed

Related Concept Videos

Solubility03:00

Solubility

Solution, Solubility, and Solubility Equilibrium
A solution is a homogeneous mixture composed of a solvent, the major component, and a solute, the minor component. The physical state of a solution—solid, liquid, or gas—is typically the same as that of the solvent. Solute concentrations are often described with qualitative terms such as dilute (of relatively low concentration) and concentrated (of relatively high concentration).
In a solution, the solute particles (molecules, atoms, and/or ions)...
Solubility Equilibria: Overview01:09

Solubility Equilibria: Overview

When a substance such as sodium chloride is added to water, it dissolves, forming an aqueous solution. The extent of dissolution is called solubility. The process of dissolution can exist in equilibrium, just like other chemical processes. Solubility equilibria are also called precipitation equilibria because the process of solubility can be reversible. The reverse of the solubility process is called precipitation.
Solubility is important in biological and environmental processes. A notable...
Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...