The passivation of pyrrhotite by surface coating

The potential of triethylenetetramine (TETA) to inhibit the oxidation of three pyrrhotites, Garson, McCreedy and Po-97 has been studied systematically and confirmed by comparing the release of Fe and SO4(2-) from samples with and without coating treatment. Each sample, original or coated by TETA, was exposed to oxygen, 1 x 10(-3) M FeCl3, and Acidithiobacillus ferrooxidans, respectively, for specific oxidation periods. Both abiotic and biotic oxidation of samples treated by this passivating agent has been reduced significantly in this study. Under the aerobic condition, lower concentrations of ferric, total Fe or SO4(2-) were obtained from the coated samples than those from the uncoated samples. In the presence of 1 x 10(-3) M FeCl3 at 30 degrees C, TETA was able to reduce oxidation rates of Garson, McCreedy and Po-97 by 83%, 79%, and 81% (based on Fe release), respectively. A higher pH, lower Eh, and lower concentrations of total Fe and SO4(2-) were also observed in the biotic oxidation of coated Garson by Acidithiobacillus ferrooxidans. The protection of pyrrhotite surface from oxidant attack by TETA barrier and the alkaline property of this coating agent can be used to interpret the inhibition of oxidation.