Thermoresponsive gelatin/monomethoxy poly(ethylene glycol)-poly(D,L-lactide) hydrogels: formulation,...

The primary objective of this study was to prepare novel thermoresponsive binary component hydrogels composed of gelatin and monomethoxy poly(ethylene glycol)-poly(D,L-lactide) (MPEG-PDLLA) diblock copolymer and to obtain optimal formulations capable of forming gels upon a narrow temperature range between body temperature and room temperature.

MPEG-PDLLA diblock copolymers with a lower critical solution temperature (LCST) feature were synthesized by using a ring-opening polymerization method. The starting weight ratio of MPEG/DLLA was varied to obtain a series of copolymers with a wide range of molecular weight and hydrophilicity. The copolymers were characterized by 1H nuclear magnetic resonance (1H NMR) and thermogravimetric analysis. MPEG (2K)-PDLLA (1:4) was chosen to construct hydrogels with gelatin. To obtain optimal thermoresponsive formulation, various hydrogels were formulated and quantified in terms of sol-gel phase transition kinetics and rheological properties. Selected hydrogels were studied as drug carrier for gentamicin sulfate.

Gelatin/MPEG-PDLLA hydrogels underwent gelation in less than 15 min when 30 wt.% MPEG (2K)-PDLLA (1:4) was mixed with 10, 50, or 100 mg/mL gelatin. Hydrogels showed rapid gelation when 100 mg/mL gelatin was mixed with 15, 20, or 25 wt.% MPEG-PDLLA as temperature fell from 37 degrees C to room temperature. The viscosity of hydrogels depended on the frequency applied in the rheological tests, the environment temperature, and the concentration of both polymer components. The time needed for 50% gentamicin sulfate release was 5 days or longer at room temperature, and the release lasted up to 40 days. 1H NMR confirmed that MPEG-PDLLA hydrolyzed under in vitro situations.

The incorporation of a second polymer component MPEG-PDLLA into the gelatin hydrogel could modify the thermal characteristic of gelatin and the resulting binary component hydrogels obtained different thermal characteristics from the individual polymer components. Formulation of gelatin/MPEG-PDLLA hydrogels could be varied for obtaining such gels that can undergo gelation promptly upon a narrow temperature change.