Fine route for an efficient removal of 2,4-dichlorophenoxyacetic acid (2,4-D) by zeolite-supported TiO2

Zeolites HY, Hbeta and HZSM-5 with different physico-chemical properties were chosen as support for TiO2 to illustrate their adsorption, dispersion and electronic structure in photocatalysis. The extent of TiO2 loading was monitored by XRD and BET surface area measurements. The adsorption capacity of HY zeolite was found to be high and hence chosen for further modification to continue the investigation. Photodegradation kinetics were carried out with 2,4-dichlorophenoxyacetic acid (2,4-D) in aqueous solution. The extent of 2,4-D degradation on TiO2/HY loading revealed the importance of adsorption in photocatalysis. Mineralisation studies on all three zeolites with 1 wt.% TiO2 loading demonstrated the good dispersion properties of TiO2/HY. Its photocatalytic activity was found to be excellent with formulated 2,4-D. Comparison of relative photonic efficiencies demonstrated that supported photocatalysts exhibited higher activity than some of the commercial photocatalysts. The high activity of supported TiO2 is due to synergistic effects of improved adsorption of 2,4-D and efficient delocalisation of photogenerated electrons by zeolite support.