Quantitative chemical analysis of ocular melanosomes in the TEM

Melanosomes in retinal tissues of a human, monkey and rat were analyzed by EDX in the TEM. Samples were prepared by ultramicrotomy at different thicknesses. The material was mounted on Al grids and samples were analyzed in a Zeiss 912 TEM equipped with an Omega filter and EDX detector with ultrathin window. Melanosomes consist of C and O as main components, mole fractions are about 90 and 3-10 at.%, respectively, and small mole fraction ratios, between 2 and 0.1 at.%, of Na, Mg, K, Si, P, S, Cl, Ca. All elements were measured quantitatively by standardless EDX with high precision. Mole fractions of transition metals Fe, Cu and Zn were also measured. For Fe a mole fraction ratio of less than 0.1at.% was found and gives the melanin its paramagnetic properties. Its mole fraction is however close to or below the minimum detectable mass fraction of the used equipment. Only in the human eye and only in the retinal pigment epitelium (rpe) the mole fractions of Zn (0.1 at.% or 5000 microg/g) and Cu were clearly beyond the minimum detectable mass fraction. In the rat and monkey eye the mole fraction of Zn was at or below the minimum detectable mass fraction and could not be measured quantitatively. The obtained results yielded the chemical composition of the melanosomes in the choroidal tissue and the retinal pigment epitelium (rpe) of the three different species. The results of the chemical analysis are discussed by mole fraction correlation diagrams. Similarities and differences between the different species are outlined. Correlation behavior was found to hold over species, e.g. the Ca-O correlation. It indicates that Ca is bound to oxygen rich sites in the melanin. These are the first quantitative analyses of melanosomes by EDX reported so far. The quantitative chemical analysis should open a deeper understanding of the metabolic processes in the eye that are of central importance for the understanding of a large number of eye-related diseases. The chemical analysis also allows a correlation with structural changes observed at the various regions of the eye.