Spontaneous formation of polymer nanoparticles by good-solvent evaporation as a nonequilibrium process

Hiroshi Yabu1, Takeshi Higuchi, Kuniharu Ijiro

  • 1Nanotechnology Research Center, Hokkaido University, N21W10, Kita-ku, Sapporo, Hokkaido 001-0021, Japan.

Chaos (Woodbury, N.Y.)
|January 7, 2006
PubMed

More Related Videos

Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization09:02

Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization

Published on: July 9, 2015

Flash NanoPrecipitation for the Encapsulation of Hydrophobic and Hydrophilic Compounds in Polymeric Nanoparticles10:12

Flash NanoPrecipitation for the Encapsulation of Hydrophobic and Hydrophilic Compounds in Polymeric Nanoparticles

Published on: January 7, 2019

Related Concept Videos

Energetics of Solution Formation02:35

Energetics of Solution Formation

The formation of a solution is an example of a spontaneous process, which is a process that occurs under specified conditions without energy from some external source.
When the strengths of the intermolecular forces of attraction between solute and solvent species in a solution are no different than those present in the separated components, the solution is formed with no accompanying energy change. Formation of the solution requires the solute–solute and solvent–solvent electrostatic forces to...
The Colloidal State01:29

The Colloidal State

The formation of a colloidal system is exemplified by an aqueous solution containing Cl− ions is introduced to another containing Ag+ ions, resulting in the precipitation of solid AgCl as extremely tiny crystals. Instead of settling out as a filterable precipitate, these crystals remain suspended in the liquid, showcasing a colloidal system.A colloidal system involves colloidal particles within the approximate range of 1 to 1000 nm in at least one dimension, dispersed in a medium called the...
Intermolecular Forces in Solutions02:28

Intermolecular Forces in Solutions

The formation of a solution is an example of a spontaneous process, a process that occurs under specified conditions without energy from some external source.
When the strengths of the intermolecular forces of attraction between solute and solvent species in a solution are no different than those present in the separated components, the solution is formed with no accompanying energy change. Such a solution is called an ideal solution. A mixture of ideal gases (or gases such as helium and argon,...
Polymers02:34

Polymers

The word polymer is derived from the Greek words “poly” which means “many” and “mer” which means “parts”. Polymers are long chains of molecules composed of repeating units of smaller molecules, known as monomers. They either occur naturally, such as DNA and proteins, or can be constructed synthetically, like plastics. They have varied structural characteristics, such as linear chains, branched chains, or complex networks, that contribute to the properties that they exhibit. Additionally,...
Colloidal precipitates01:09

Colloidal precipitates

The high insolubility of some precipitates can result in an unfavorable relative supersaturation. This can lead to colloidal particles with a large surface-to-mass ratio, where adsorption is promoted. For instance, in the precipitation of silver chloride, silver ions are adsorbed on the surface of the colloidal particles, forming a primary layer. This layer attracts ions of opposite charge (such as nitrate ions), forming a diffuse secondary layer of adsorbed ions. This electric double layer...
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta catalyst, high molecular...