Activation processes and polyethylene formation on a phillips model catalyst studied by laser ablation, laser...

Since the discovery of the Phillips catalysts, there still is much uncertainty concerning their activation, their molecular structure, the nature of the active chromium sites, and the polymerization mechanisms. Surface techniques are not easy to be used for such study according to the nonconductive behavior of the support. Therefore, model Phillips catalyst is elaborated by spin coating a trivalent chromium precursor on a silicon wafer. The surface characterization of this model catalyst is conducted by laser ablation mass spectrometry (LA-MS), laser desorption/ionization mass spectrometry (LDI-MS), and static secondary ion mass spectrometry (s-SIMS), at different steps of its preparation. To validate our approach, a comparison is also made between the model and the real Philips catalyst. Moreover, the model catalyst efficiency for polyethylene synthesis is evaluated and allows us to discuss the validity of the mechanisms previously proposed to explain the catalytic process. The characterization of Phillips model catalyst by mass spectrometry allows us to better understand the activation processes of such catalyst. Depending on the activation temperature, chromium oxide species are formed and anchored at the support surface. They consist mainly in mono-chromium sites at high temperature. The chromium valence is hexavalent. This model catalyst is active for the polymerization of ethylene. A pseudo-oligomer molecular weight distribution is observed by LA-MS, whereas s-SIMS allows us to elucidate the anchorage of the polymer at activate chromium surface sites.