Stress corrosion cracking of NiTi in artificial saliva

Jianqiu Wang1, Nianxing Li, Guangbin Rao

  • 1Environmental Corrosion Center, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China. jiqwang@imr.ac.cn

Dental Materials : Official Publication of the Academy of Dental Materials
|February 10, 2006
PubMed
Abstract

More Related Videos

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Applying Dynamic Strain on Thin Oxide Films Immobilized on a Pseudoelastic Nickel-Titanium Alloy09:35

Applying Dynamic Strain on Thin Oxide Films Immobilized on a Pseudoelastic Nickel-Titanium Alloy

Published on: July 28, 2020

Related Concept Videos

2° Amines to N-Nitrosamines: Reaction with NaNO201:20

2° Amines to N-Nitrosamines: Reaction with NaNO2

Secondary amines react with nitrous acid to form N-nitrosamines, as depicted in Figure 1. Nitrous acid, a weak and unstable acid, is formed in situ from an aqueous solution of sodium nitrite and strong acids, such as hydrochloric acid or sulfuric acid, in cold conditions. In the presence of an acid, the nitrous acid gets protonated. The subsequent loss of water results in the formation of the electrophile known as nitrosonium ion.
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Overview01:26

1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Overview

Nitrous acid and nitric acids are two types of acids containing nitrogen, among which nitrous acid is weaker than nitric acid. Nitrous acid with a pKa value of 3.37 ionizes in water to give a nitrite ion and the hydronium ion.
The nitrous acid is unstable. Hence, it is formed in situ from a solution of sodium nitrite and cold aqueous acids such as hydrochloric or sulfuric acid. In an acidic solution, the –OH group of nitrous acid undergoes protonation to give oxonium ion, followed by water loss...