Structural, optical, and magnetic properties of Mn-doped ZnO thin film
1Center for Advanced Optoelectronic Functional Material Research, Northeast Normal University, Changchun, China.
Abstract:
The Zn(1-x)Mn(x)O (x = 0, 0.16, and 0.25) thin films were grown on fused quartz substrates by reactive magnetron cosputtering. X-ray-diffraction measurement revealed that all the films were single phase and had wurtzite structure with c-axis orientation. As Mn concentration increased in the Zn(1-x)Mn(x)O films, the c-axis lattice constant and band-gap energy increased gradually. In Raman-scattering studies, an additional Mn-related vibration mode appeared at 520 cm(-1). E(2H) phonon line of Zn(1-x)Mn(x)O alloy was broadened asymmetrically and redshifted as a result of microscopic structural disorder induced by Mn(2+) random substitution. The Zn(0.84)Mn(0.16)O film exhibited a ferromagnetic characteristic with a Curie temperature of approximately 62 K. However, with increasing Mn concentration to 25 at. %, ferromagnetism disappeared due to the enhanced antiferromagnetic superexchange interactions between neighboring Mn(2+) ions.
Related Concept Videos
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.
01:26Diamagnetism
Diamagnetism was discovered by Anton Brugmans in 1778 when he observed that bismuth gets repelled by magnetic fields, thus theorizing that diamagnets get repelled by magnets.