The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the generated carbocation,...

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...

The mechanism for anionic chain-growth polymerization involves initiation, propagation, and termination steps. In the initiation step, a nucleophilic anion, such as butyl lithium, initiates the polymerization process by attacking the π bond of the vinylic monomer. As a result, a carbanion, stabilized by the electron‐withdrawing group, is generated. The resulting carbanion acts as a Michael donor in the propagation step and attacks the second vinylic monomer, which acts as a Michael acceptor.

Polymer samples typically consist of macromolecular chains with a distribution of lengths, resulting in a range of molar masses rather than a single discrete value. Conventional descriptors such as the number-average molar mass and weight-average molar mass quantify this distribution but do not fully capture polymer behavior in solution..The viscosity-average molar mass provides a more realistic description of polymer behavior in solution because it accounts for the enhanced contribution of...