Poly(epsilon-caprolactone)/chitin and poly(epsilon-caprolactone)/chitosan blend films with compositional gradients:...

Poly(epsilon-caprolactone) (PCL)/chitin and PCL/chitosan blend films with compositional gradients were successfully fabricated by a dissolution/diffusion method; that is, repeatedly pouring the PCL/chitin (or PCL/chitosan) blend solutions, with variable composition, onto polysaccharide layers. The compositional gradient structure in the resulting films was characterized by polarized optic microscopy, ATR-FT-IR and trans-FT-IR microscopic spectroscopy. Enzymatic degradability of the PCL/chitin and PCL/chitosan blend films with compositional gradients in the presence of lysozyme was compared with those of homogeneous films and two-layer films. It was found that the degradation rate of PCL/chitin blend films with a compositional gradient was far lower than that of the neat chitin film, whereas the degradation rate of PCL/chitosan blend films with a compositional gradient was close to that of the neat chitosan film. The suppression of the chitosan crystallization, which accelerates the enzymatic degradation, at the surface of PCL/chitosan films with a compositional gradient was much more severe than that for PCL/chitin films with a compositional gradient.