Viscoelastic effects on early stage of spinodal decomposition in dynamically asymmetric polymer blends

Mikihito Takenaka1, Hiroyuki Takeno, Takeji Hashimoto

  • 1Department of Polymer Chemistry, Graduate School of Engineering, Kyoto University, Kyoto 606-8501, Japan. takenaka@alloy.polym.kyoto-u.ac.jp

The Journal of Chemical Physics
|March 18, 2006
PubMed

More Related Videos

Molecular Entanglement and Electrospinnability of Biopolymers07:59

Molecular Entanglement and Electrospinnability of Biopolymers

Published on: September 3, 2014

Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing09:39

Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing

Published on: June 28, 2024

Related Concept Videos

Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Anionic Chain-Growth Polymerization: Mechanism01:04

Anionic Chain-Growth Polymerization: Mechanism

The mechanism for anionic chain-growth polymerization involves initiation, propagation, and termination steps. In the initiation step, a nucleophilic anion, such as butyl lithium, initiates the polymerization process by attacking the π bond of the vinylic monomer. As a result, a carbanion, stabilized by the electron‐withdrawing group, is generated. The resulting carbanion acts as a Michael donor in the propagation step and attacks the second vinylic monomer, which acts as a Michael acceptor.
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...