A simple route utilizing surfactant-assisted templating sol-gel process for synthesis of mesoporous Dy2O3 nanocrystal

A simple route of combined sol-gel process with surfactant-assisted templating technique was successfully employed for the first time to synthesize nanocrystalline mesoporous Dy(2)O(3) with narrow monomodal pore size distribution under mild conditions. The nanocrystalline Dy(2)O(3) with monomodal mesoporous characteristic was ultimately achieved by controlling the hydrolysis and condensation steps of dysprosium n-butoxide modified with acetylacetone in the presence of laurylamine hydrochloride surfactant aqueous solution. The synthesized material was methodically characterized by thermogravimetry and differential thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), selected-area electron diffraction (SAED), N(2) adsorption-desorption, Brunauer-Emmett-Teller (BET) surface area analysis, and Barrett-Joyner-Halenda (BJH) pore size distribution analysis. The particle size of the synthesized Dy(2)O(3) in nanosized range obtained from the SEM and HRTEM micrographs was in good accordance with the crystallite size estimated from the XRD result. The N(2) adsorption-desorption result exhibited hysteresis pattern with single loop, indicating the existence of monomodal mesopore. The extremely narrow pore size distribution with mean pore diameter in the mesopore region of the synthesized Dy(2)O(3) was also confirmed by the BJH result.