Measuring the Mechanical Properties of Glass Fiber Reinforcement Polymer Composite Laminates Obtained by Different Fabrication Processes
09:54

Measuring the Mechanical Properties of Glass Fiber Reinforcement Polymer Composite Laminates Obtained by Different Fabrication Processes

Published on: June 30, 2023

Flexural properties of glass fibre reinforced acrylic resin polymers

I H Tacir1, J D Kama, M Zortuk

  • 1Department of Prosthodontics, Faculty of Dentistry, Dicle University, Diyarbakir, Turkey.

Australian Dental Journal
|May 4, 2006
PubMed
Abstract

More Related Videos

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior11:07

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior

Published on: June 27, 2018

Stereolithographic 3D Printing with Renewable Acrylates08:28

Stereolithographic 3D Printing with Renewable Acrylates

Published on: September 12, 2018

Related Concept Videos

Fiber Reinforced Concrete01:22

Fiber Reinforced Concrete

Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...
Classification and Mechanical Properties of Synthetic Polymers01:28

Classification and Mechanical Properties of Synthetic Polymers

Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
Members Made of Elastoplastic Material01:19

Members Made of Elastoplastic Material

The behavior of elastoplastic materials under bending stresses, particularly in structural members with rectangular cross-sections, is crucial for predicting material responses and understanding failure modes. Initially, when a bending moment is applied, the stress distribution across the section follows Hooke's Law and is linear and elastic. This distribution means the stress increases from the neutral axis to the maximum at the outer fibers, up to the elastic limit.
As the bending moment...
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
Poisson's Ratio01:23

Poisson's Ratio

Poisson's ratio is a material property that indicates their stress response. It explains the connection between the elongation or compression a material undergoes in the direction of an applied force and the contraction or expansion it experiences perpendicular to that force. When a slender bar is loaded axially, it stretches in the direction of the force and contracts laterally. Poisson's ratio is the negative ratio of this lateral contraction to the axial elongation. The negative sign ensures...