Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent
11:14

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

Published on: February 21, 2017

Anomalous transient leaching behavior of metals solidified/stabilized by pozzolanic fly ash

Lucy Mar Camacho1, Stuart H Munson-McGee

  • 1Department of Chemical Engineering, New Mexico State University, Las Cruces, NM 88003, USA. lcamacho@nmsu.edu

Journal of Hazardous Materials
|May 9, 2006
PubMed

More Related Videos

Resource Recycling of Red Soil to Synthesize Fe2O3/FAU-type Zeolite Composite Material for Heavy Metal Removal05:52

Resource Recycling of Red Soil to Synthesize Fe2O3/FAU-type Zeolite Composite Material for Heavy Metal Removal

Published on: June 2, 2022

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels07:13

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

Published on: April 16, 2017

Related Concept Videos

Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is a...
Additives and Fillers in Concrete01:29

Additives and Fillers in Concrete

Additives and fillers are integral to enhancing the properties of concrete. Pozzolans and blast-furnace slag are additives or admixtures due to their reactions with calcium hydroxide released during cement hydration. Fillers, which are finely ground and similar in fineness to Portland cement, improve concrete attributes such as workability density, and reduce capillary bleeding or cracking. Some fillers possess hydraulic properties or participate in benign reactions within the cement paste.
The...
Microbial Leaching01:27

Microbial Leaching

Microbial leaching, also known as bioleaching, is an environmentally favorable method for extracting metals from low-grade ores using specific microorganisms. This biotechnological approach is particularly valuable for mining operations targeting copper, gold, and uranium, where traditional extraction methods may be economically or environmentally impractical.Copper Leaching and Microbial CatalysisIn copper bioleaching, crushed ore is arranged into heaps and irrigated with a dilute sulfuric...
Alkali Aggregate Reaction in Concrete01:26

Alkali Aggregate Reaction in Concrete

The alkali-aggregate reaction in concrete involves natural siliceous minerals in aggregates reacting with alkaline hydroxides derived from cement alkalis. This reaction forms an alkali-silica gel that absorbs water, swells, and increases in volume, which is confined by the surrounding cement paste, creating internal pressures that crack and disrupt the concrete. The extent of expansion and damage can be partly attributed to the alkali-silica reaction's osmotic hydraulic pressure and the...
Acid Mine Drainage01:19

Acid Mine Drainage

Mining activities that disturb sulfide-rich rocks, particularly those containing pyrite (FeS₂), initiate a cascade of geochemical and microbiological processes with serious environmental implications. When exposed to air and water, pyrite undergoes oxidation, releasing sulfate, ultimately forming sulfuric acid and mobilizing heavy metals into surrounding water systems. This phenomenon, known as acid mine drainage (AMD), results in low pH waters laden with toxic elements that threaten aquatic...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...