Retinol-encapsulated low molecular water-soluble chitosan nanoparticles

This aim of this study was to encapsulate retinol into chitosan nanoparticles and reconstitute it into aqueous solution. Retinol-encapsulated chitosan nanoparticles were prepared for application of cosmetic and pharmaceutical applications. Retinol-encapsulated chitosan nanoparticle has a spherical shape and its particle sizes were around 50-200 nm according to the drug contents. Particle size was increased according to the increase of drug contents. Solubility of retinol is able to increase by encapsulation into chitosan nanoparticles more than 1600-fold. It was suggested that retinol was encapsulated into chitosan nanoparticles by ion complex as a result of FT-IR spectra. Specific peak of chitosan at 1590 cm(-1) was divided to semi-doublet due to the electrostatic interaction between amine group of chitosan and hydroxyl group of retinol. At (1)H NMR spectra, specific peaks of retinol disappeared when retinol-encapsulated chitosan nanoparticles were reconstituted into D(2)O while specific peaks both of retinol and chitosan appeared at D(2)O/DMSO (1/4, v/v) mixture. XRD patterns also showed that crystal peaks of retinol were disappeared by encapsulation into chitosan nanoparticles. Retinol-encapsulated nanoparticles were completely reconstituted into aqueous solution as same as original aqueous solution and zeta potential of reconstituted chitosan nanoparticles was similar to their original solution. At HPLC study, retinol was stably and efficiently encapsulated into chitosan nanoparticles.