Shape-controlled synthesis of ternary chalcogenide ZnIn2S4 and CuIn(S,Se)2 nano-/microstructures via facile solution...

We demonstrated in this paper the shape-controlled synthesis of ZnIn2S4, CuInS2, and CuInSe2 nano- and microstructures through a facile solution-based route. One-dimensional ZnIn2S4 nanotubes and nanoribbons were synthesized by a solvothermal method with pyridine as the solvent, while ZnIn2S4 solid or hollow microspheres were hydrothermally prepared in the presence of a surfactant such as cetyltrimethylammonium bromide (CTAB) or poly(ethylene glycol) (PEG). The mechanisms related to the phase formation and morphology control of ZnIn2S4 are proposed and discussed. The UV-vis absorption spectra show that the as-prepared nano- and micromaterials have strong absorption in a wide range from UV to visible light and that their band gaps are somewhat relevant to the size and morphology. The photoluminescence measurements of the ZnIn2S4 microspheres at room temperature reveal intense excitation at approximately 575 nm and red emission at approximately 784 nm. Furthermore, CuInS2 and CuInSe2 with different morphologies such as spheres, platelets, rods, and fishbone-like shapes were also obtained by similar hydrothermal and solvothermal synthesis.