Comparison and performance characteristics of 3 different knots when tied with 2 suture materials used for shoulder
Andrew T Mahar1, Darius M Moezzi, Fred Serra-Hsu
1Department of Orthopaedic Surgery, University of California San Diego, San Diego, California, USA. amahar@chsd.org
Purpose:
To compare the performance of a standard suture material with that of a new material across several arthroscopic knot configurations.
Methods:
Three knots were evaluated (Duncan loop, Weston, and San Diego knots) with the use of 2 suture materials (No. 2 Ethibond [Ethicon, Somerville, NJ] and No. 2 Force Fiber [Stryker Endoscopy, San Jose, CA]). Ten samples were tested for each knot and suture configuration. Samples were pretensioned to 10 N and were mechanically loaded from 10 to 45 N for 1,000 cycles. The number of cycles to 3 mm of loop elongation was recorded as "early" slippage. Intact knots with no evidence of early slippage were then subjected to a load-to-failure test so that the ultimate failure strength of the knot/material could be determined.
Results:
Force Fiber knots required a statistically greater number of cycles to reach 3 mm of slippage compared with Ethibond knots (P < .0001). A single Force Fiber knot experienced 3 mm of displacement during cyclic loading; all others survived to 1,000 cycles. One third of all Ethibond knots were displaced to 3 mm during cyclic loading. For Ethibond sutures, no significant differences in ultimate failure strength were observed between knots (average, 143 N across knot types). For Force Fiber sutures, the San Diego knot (279 +/- 41 N) was statistically similar in ultimate failure strength to the Weston knot (254 +/- 41 N), but it was significantly stronger than the Duncan knot (224 +/- 70 N) (P < .03).
Conclusions:
The higher failure loads associated with Force Fiber may allow the surgeon to increase suture tension during knot tying, thereby creating a tighter knot. Loop elongation with Force Fiber occurred at loads that were greater than the typical breakage load for No. 2 Ethibond. Force Fiber is a new material that may be useful for various arthroscopic procedures.
Clinical Relevance:
Force Fiber provided increased biomechanical stability compared with Ethibond regardless of knot type. The cost benefit of using very strong yet very stiff sutures must be clinically evaluated.