Influence of initiator and different polymerisation conditions on performance of molecularly imprinted polymers

Irene Mijangos1, Fernando Navarro-Villoslada, Antonio Guerreiro

  • 1Institute of BioScience and Technology, Cranfield University, Silsoe, Bedfordshire MK45 4DT, UK. i.mijangos.s03@cranfield.ac.uk

Biosensors & Bioelectronics
|June 20, 2006
PubMed

More Related Videos

Polymer Microarrays for High Throughput Discovery of Biomaterials13:37

Polymer Microarrays for High Throughput Discovery of Biomaterials

Published on: January 25, 2012

Anionic Polymerization of an Amphiphilic Copolymer for Preparation of Block Copolymer Micelles Stabilized by π-π Stacking Interactions10:53

Anionic Polymerization of an Amphiphilic Copolymer for Preparation of Block Copolymer Micelles Stabilized by π-π Stacking Interactions

Published on: October 10, 2016

Related Concept Videos

Determination of Molar Masses of Polymers I01:24

Determination of Molar Masses of Polymers I

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Olefin Metathesis Polymerization: Overview01:13

Olefin Metathesis Polymerization: Overview

Recently, the development of olefin metathesis polymerization advanced the field of polymer synthesis. Simply put, the reorganization of substituents on their double bonds between two olefins in the presence of a catalyst is known as the olefin metathesis reaction. The use of metathesis reaction for polymer synthesis is called olefin metathesis polymerization.
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists of a...
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
Cationic Chain-Growth Polymerization: Mechanism00:57

Cationic Chain-Growth Polymerization: Mechanism

The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the generated carbocation,...
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...