Dynamics of the interaction of vapor-deposited copper with alkanethiolate monolayers: bond insertion, complexation,...

We have investigated the interaction of vapor-deposited copper with -CH3, -OH, -OCH3, -COOH, and -CO2CH3 terminated alkanethiolate self-assembled monolayers (SAMs) adsorbed on polycrystalline Au using time-of-flight secondary ion mass spectrometry and density functional theory calculations. For -OH, -COOH, and -CO2CH3 terminated SAMs measurements indicate that for all copper coverages there is a competition between Cu atom bond insertion into C-O bonds, stabilization at the SAM/vacuum interface, and penetration to the Au/S interface. In contrast, on a -OCH3 terminated SAM Cu only weakly interacts with the methoxy group and penetrates to the Au substrate, while for a -CH3 terminated SAM deposited copper only penetrates to the Au/S interface. The insertion of copper into C-O terminal group bonds is an activated process. We estimate that the barriers for Cu insertion are 55 +/- 5 kJ mol(-1) for the ester, 50 +/- 5 kJ mol(-1) for the acid, and 55 +/- 5 kJ mol(-1) for the hydroxyl terminated SAMs. The activation barrier for the copper insertion is much higher for the -OCH3 SAM. Copper atoms with energies lower than the activation barrier partition between complexation (weak interaction) with the terminal groups and penetration through the monolayer to the Au/S interface. Weakly stabilized copper atoms at the SAM/vacuum interface slowly penetrate through the monolayer. In contrast to the case of Al deposition, C-O bond insertion is favored over C=O, C-H, and C-C bond insertion.