First-principles study of the diffusion of hydrogen in ZnO

Zinc oxide, a wide-gap semiconductor, typically exhibits n-type conductivity even when nominally undoped. The nature of the donor is contentious, but hydrogen is a prime candidate. We present ab initio calculations of the migration barrier for H, yielding a barrier of less than approximately 0.5 eV. This indicates isolated hydrogen is mobile at low temperature and that thermally stable H-related donors must logically be trapped at other defects. We argue this is also true for other oxides where H is a shallow donor.